SDS Volume
Volume 70. Solubility of Gases in Glassy Polymers, p None
Source Publication
Volkov, V. V.; Bokarev, A. K.; Durgaryan, S. G.; Nametkin, N. S.; Dokl. Akad. Nauk USSR 282, 641 (1985).
Plate, N. A.; Bokarev, A. K.; Kaliuzhnyi, N. E.; Litvinova, E. G.; Khotimskii, V. S.; Volkov, V. V.; Yampol'skii, Yu. P.; J. Membr. Sci. 60, 13 (1991).
Conditions:
Room Temp:
298
$\pu{K}$
Pressure:
0 - 0.7
$\pu{MPa}$
Compiler:
Methodology:
Sorption was measured using a gravimetric technique described in [1].
Sample Information:
- No information given.
Methodology Citation
1 Volkov, V. V.; Bokarev, A. K.; Durgaryan, S. G.; Vysokomol. Soedin. Ser. A 26, 1294 (1984).
System Components:
- Xenon, $\ce{ Xe }$; [7440-63-3] NIST WebBook
- Carbon dioxide, $\ce{ CO2 }$; [124-38-9] NIST WebBook
- Nitrous Oxide, [10024-97-2] NIST WebBook
- Propane, $\ce{ C3H8 }$; [74-98-6] NIST WebBook
- Poly(vinyltrimethyl silane) (PVTMS), $\ce{ (C5H12Si)n }$; [25036-32-2] NIST WebBook
Experimental Data
| $k_{\rm{H}}$ ($\pu{cm3(STP) cm-3 cmHg-1}$) | $C_{\rm{H}}^{\prime}$ ($\pu{cm3/cm3}$) | $b$ ($\pu{cmHg}$) |
|---|---|---|
| 0.0120 | 18.5 | 4.1 x 10-3 |
| 4.6 x 10-3 | 28.7 | 1.1 x 10-3 |
| 0.014 | 13.1 | 2.9 x 10-3 |
| 1.13 x 10-3 | 5.2 | 0.191 |