Volume 70. Solubility of Gases in Glassy Polymers, p 1417
Source Publication
Ilinitch, O. M.; Semin, G. L.; Chertova, M. V.; Zamaraev, K. I.; J. Membr. Sci. 66, 1-8 (1992).
Conditions:
Room Temp:
293.2
$\pu{K}$
Pressure:
0 - 100
$\pu{MPa}$
% mole frac. 2:
(I) 75
%
% mole frac. 2:
(II) 25
%
Compiler:
Methodology:
The conventional McBain sorption spring balance was used.
Sample Information:
- All the gases had a purity $\pu{\gt 99.9\%}$.
- The co-polymer was prepared via oxidative co-polycondensation of two monomers. The purity of product $\pu{99.9\%}$, it had $d = \pu{1.10 g mL-1}$ and $T_{\rm{g}} = \pu{754 K}$.
Measurement Errors:
Ambient temperature: ±0.1 K
Solubility (v/v): 0.1 (compiler)
Pressure: ±0.2 kPa
System Components:
- Methane, $\ce{ CH4 }$ ; [74-82-8] NIST WebBook
- Copoly(2,6-dimethyl-1,4-phenylene oxide-2,6-diphenyl-1,4-phenylene oxide)
Experimental Data
Solubility of methane in the copolymer
| $P_{1}$ ($\pu{kPa}$) | S ($\pu{cm3(g) cm-3(s) atm-1}$) |
|---|---|
| 34.0 | 0.4 |
| 53.3 | 0.8 |
| 66.7 | 1.2 |
| 82.6 | 1.5 |
Download Data
System Components:
- Ethane, $\ce{ C2H6 }$ ; [74-84-0] NIST WebBook
- Copoly(2,6-dimethyl-1,4-phenylene oxide-2,6-diphenyl-1,4-phenylene oxide)
Experimental Data
Solubility of ethane in the copolymer
| $P_{1}$ ($\pu{kPa}$) | S ($\pu{cm3(g) cm-3(s) atm-1}$) |
|---|---|
| 7.3 | 1.1 |
| 14.0 | 1.4 |
| 21.3 | 2.1 |
| 26.9 | 2.5 |
| 34.4 | 3.6 |
Download Data
System Components:
- Ethene, $\ce{ C2H4 }$ ; [74-85-1] NIST WebBook
- Copoly(2,6-dimethyl-1,4-phenylene oxide-2,6-diphenyl-1,4-phenylene oxide)
Experimental Data
Solubility of ethene in the copolymer
| $P_{1}$ ($\pu{kPa}$) | S ($\pu{cm3(g) cm-3(s) atm-1}$) |
|---|---|
| 8.0 | 1.0 |
| 12.0 | 1.3 |
| 14.3 | 1.6 |
| 18.7 | 1.8 |
| 22.0 | 2.1 |
| 26.0 | 2.6 |
| 34.7 | 3.2 |
Download Data
System Components:
- Propane, $\ce{ C3H8 }$ ; [74-98-6] NIST WebBook
- Copoly(2,6-dimethyl-1,4-phenylene oxide-2,6-diphenyl-1,4-phenylene oxide)
Experimental Data
Solubility of propane in the copolymer
| $P_{1}$ ($\pu{kPa}$) | S ($\pu{cm3(g) cm-3(s) atm-1}$) |
|---|---|
| 5.1 | 3.1 |
| 10.0 | 4.4 |
| 14.0 | 5.1 |
| 20.0 | 5.9 |
| 24.0 | 6.6 |
| 29.3 | 7.2 |
| 34.4 | 7.8 |
| 40.0 | 8.4 |
| 46.6 | 9.4 |
| 53.3 | 10.2 |
| 61.3 | 11.2 |
Download Data
System Components:
- Propene, $\ce{ C3H6 }$ ; [115-07-1] NIST WebBook
- Copoly(2,6-dimethyl-1,4-phenylene oxide-2,6-diphenyl-1,4-phenylene oxide)
Experimental Data
Solubility of propene in the copolymer
| $P_{1}$ ($\pu{kPa}$) | S ($\pu{cm3(g) cm-3(s) atm-1}$) |
|---|---|
| 1.6 | 2.0 |
| 4.0 | 2.9 |
| 6.7 | 4.0 |
| 10.6 | 4.9 |
| 14.0 | 5.6 |
| 20.0 | 6.8 |
| 26.7 | 7.6 |
| 33.3 | 9.0 |
| 38.7 | 9.6 |
| 53.3 | 11.5 |